Stress corrosion cracking behavior of buried oil and gas pipeline steel under the coexistence of magnetic field and sulfate-reducing bacteria Open?Access
文章信息
作者：Jian-Yu He, Fei Xie, Dan Wang, Guang-Xin Liu, Ming Wu, Yue Qin
作者單位：
投稿時間：
引用方式：Jian-Yu He, Fei Xie, Dan Wang, Guang-Xin Liu, Ming Wu, Yue Qin, Stress corrosion cracking behavior of buried oil and gas pipeline steel under the coexistence of magnetic field and sulfate-reducing bacteria, Petroleum Science, Volume 21, Issue 2, 2024, Pages 1320-1332, https://doi.org/10.1016/j.petsci.2023.10.013.
文章摘要
Abstract: Magnetic field and microorganisms are important factors influencing the stress corrosion cracking (SCC) of buried oil and gas pipelines. Once SCC occurs in buried pipelines, it will cause serious hazards to the soil environment. The SCC behavior of X80 pipeline steel under the magnetic field and sulfate-reducing bacteria (SRB) environment was investigated by immersion tests, electrochemical tests, and slow strain rate tensile (SSRT) tests. The results showed that the corrosion and SCC sensitivity of X80 steel decreased with increasing the magnetic field strength in the sterile environment. The SCC sensitivity was higher in the biotic environment inoculated with SRB, but it also decreased with increasing magnetic field strength, which was due to the magnetic field reduces microbial activity and promotes the formation of dense film layer. This work provided theoretical guidance on the prevention of SCC in pipeline steel under magnetic field and SRB coexistence.
關鍵詞
-
Keywords: Magnetic field; Sulfate-reducing bacteria; Film layer; Stress corrosion cracking; Oil and gas pipelines